WEATHER TEST RESULTS |
|
||
| SANOY S-20 QUV TEST RESULTS | ||
| (ASA: ACRYLONITRILE-STYRENE-ACRLYIC | ||
| COLOR | HOURS TESTED | DELTA E |
| WHITE | 4000 | 1.23 |
| WHITE | 2000 | 0.67 |
| REDWOOD | 3000 | 1.04 |
| GRAY | 3000 | 0.78 |
| CLAY | 3000 | 0.77 |
| BLUE | 3000 | 0.88 |
| **Tests were conducted using an independent lab firm(s). Independent lab firm(s) provided upon request. Test Method used: ASTM G 154-98-Ultraviolet Exposure-Outdoor Applications. QUV: Q-Panel, Cycles = 8 hrs. of UV @ 60 degrees C +/-5 and 4 hrs. condensation @ 50 degrees C +/-5. The typical results reported are believed to be based on reliable procedures. Due to variable conditions or methods of processing. NO GUARANTEES OR WARRANTIES ARE EXPRESSED OR IMPLIED INCLUDING THE IMPLIED WARRANTYOF MERCHANTABILITY AND FITNESS FOR PARTICULAR PURPOSE. Nor are any recommendations made to infringe on patents. SANOY is a registered trademark of Hughes Processing, Inc. | ||
|
||
| SANOY POLYMERS-XENON TEST RESULTS | ||
| MATERIAL | kj/m2 TESTED | DELTA E |
| S-33 WHITE (ASA) | 4200 | 0.23 |
| S-25 WHITE (ASA) | 3800 | 0.87 |
| SC-25 CLEAR (Impact Co-Polymer) | 3000 | 2.43 |
| S-27P Redwood (Polystyrene) | 4000 | 2.40 |
| S-27P Oak (Polystyrene) | 4000 | 1.50 |
| SC-25 Walnut (Impact Co-Polymer) | 3000 | 4.66 |
|
|
||
| **Tests were conducted using an independent lab firm(s). Independent lab firm(s) provided upon request. Test Method used: ASTM G 155-04a-Xenon Arc light apparatus for exposure of non-metallic materials. The typical results reported are believed to be based on reliable procedures. Due to variable conditions or methodsof processing. NO GUARANTEES OR WARRANTIES ARE EXPRESSED OR IMPLIED INCLUDING THE IMPLIED WARRANTY OF MERCHANTABILITY AND FITNESS FOR PARTICULAR PURPOSE. Nor are any recommendations made to infringe on patents. SANOY is a registered trademark of Hughes Processing, Inc. |
||